MJF Nylon PA11, also known as Nylon 11 or Polyamide 11, is a type of nylon material used in the Multi Jet Fusion (MJF) additive manufacturing process. It is a thermoplastic polymer known for its high strength, durability, and chemical resistance. MJF Nylon PA11 offers several desirable properties that make it suitable for various industrial applications.
Here are some key characteristics and information about MJF Nylon PA11:
Material Details
- Material Type: Nylon PA11 (Polyamide 11)
- Printing Technology: Multi Jet Fusion (MJF)
- Application: Industria
- l-grade parts, functional prototypes
Technical Properties
| Property | Value |
|---|---|
| Tensile Strength | Typically 40-50 MPa |
| Tensile Modulus | 1,500-2,500 MPa |
| Tensile Elongation | Typically 30-100% |
| Flexural Strength | 50-70 MPa |
| Flexural Modulus | 1,500-2,500 MPa |
| Heat Deflection Temperature (HDT) at 0.45 MPa | Varies depending on grade and testing conditions |
| Heat Deflection Temperature (HDT) at 1.8 MPa | Varies depending on grade and testing conditions |
These values represent the approximate range for the specified technical properties of MJF Nylon PA11. However, it's important to note that the specific values may vary depending on the grade, manufacturer, and testing conditions of the material.
MJF Nylon PA11 exhibits good tensile strength, modulus, and elongation, providing it with structural integrity and the ability to withstand external forces. The flexural strength and modulus indicate its resistance to bending or flexing forces. The heat deflection temperature (HDT) represents the temperature at which the material starts to deform under specific loads.
For precise and up-to-date technical specifications, including the HDT values under specific conditions, it is recommended to refer to the manufacturer's documentation or data sheets for the specific grade of MJF Nylon PA11 being used.