Carbon-filled PA-11 Nylon is stiffer than regular nylon and is best used for applications where a high strength-to-weight ratio is needed.
Material Details:
SLS Nylon PA11 Carbon Fiber (PA11-CF) is a highly rigid material due to its carbon fiber reinforcement. This feature makes it an excellent choice for applications that require exceptional rigidity. It is particularly suitable for lightweight designs without compromising the functionality of the part. This characteristic makes it advantageous for manufacturing various components, including motorsport parts.
Technical Properties:
| Technical properties | Value |
|---|---|
| Tensile strength | 82 MPa |
| Tensile modulus | 5900 MPa |
| Tensile elongation | 7% |
| Flexural modulus | 5800 MPa |
| HDT (0.45 MPa) | 189°C |
| HDT (1.8 MPa) | 151°C |
Please note that the provided technical properties represent the typical values for SLS Nylon PA11 Carbon Fiber.